Resistência flexural de uma resina para impressão 3D comparada a resinas acrílicas convencionais empregadas para confecção de placas estabilizadoras de mordida / Flexural resistance of 3D printing resin compared to conventional acrylic resins employed to build occlusal bite splints

Introduction: with the technological advance in dentistry, light-polymerized three-dimensional (3D) printing resins had become an alternative for the manufacture of occlusal splint splints. Objective: the present study aimed to analyze the flexural strength of a resin for 3D printing compared to conventional acrylic resins (chemically activated and thermally activated), under the influence of thermocycling. Material and method: 60 specimens were made, which were distributed in six experimental groups (n = 10), according to the resin employed (chemically activated acrylic resin, thermally activated acrylic resin and 3D printing resin) and the treatment received (control and thermocycling). The specimens were submitted to flexural strength by the three-point flexural test. Result: data analysis showed that the material factor (<0.0001) and the thermocycling factor (p = 0.0096) influenced flexural strength, however, the interaction between the two factors did not (p = 0.9728). Conclusion: it was concluded that 3D printing resins presented the lowest flexural resistance to acrylic resins, especially when submitted to thermocycling.

Introdução: com o avanço tecnológico dentro da odontologia, as resinas fotopolimerizáveis para impressão tridimensional (3D) se tornaram uma alternativa para a fabricação de dispositivos interoclusais. Objetivo: o presente trabalho teve como objetivo analisar a resistência flexural de uma resina para impressão tridimensional comparada com resinas acrílicas convencionais (quimicamente ativada e termicamente ativada), sob a influência da termociclagem. Material e método: foram confeccionados 60 corpos de prova, que foram distribuídos aleatoriamente em seis grupos experimentais (n=10), de acordo com a resina utilizada (resina acrílica ativada quimicamente, resina acrílica ativada termicamente e resina para impressão 3D) e com o tratamento recebido (controle e termociclagem). Os corpos de prova foram submetidos ao ensaio de flexão de três pontos para determinação da resistência flexural. Resultado: a análise dos dados demonstrou que o fator material (<0.0001) e o fator termociclagem (p=0.0096) influenciaram a resistência flexural, entretanto, a interação entre os dois fatores não (p=0.9728). Conclusão: deste modo podemos concluir que a resina para impressão 3D apresentou desempenho inferior às resinas acrílicas, especialmente quando submetida a termociclagem.

Y-TZP Physicochemical Properties Conditioned with ZrO2 and SiO2 Nanofilms and Bond Strength to Dual Resin Cement.

Commercial Yttria-tetragonal zirconia polycrystalline (Y-TZP) was subjected to surface treatments, and the bond strength of dual resin cement to Y-TZP and failure modes were evaluated. Disks (12 mm × 2 mm), cylinders (7 mm × 3.3 mm), and bars (25 mm × 5 mm × 2 mm) were milled from Y-TZP CAD-CAM blocks, divided into seven groups, and subjected to different surface treatments; silicatization was used as control. On the basis of the literature, this study evaluated modifications with films containing SiO2 nanoparticles and silane; SiO2+ZrO2­SiO2 (50%) and ZrO2 (50%) nanoparticles, SiO2+ZrO2/Silane-SiO2 (50%) and ZrO2 (50%) nanoparticles, and silane. Specimens were analyzed by wettability (n = 3), surface free energy (n = 3), X-ray diffraction (n = 1), Fourier transform infrared spectroscopy (FTIR) (n = 1), roughness (n = 5), shear bond test (n = 10), and dynamic modulus (n = 3). Specimens treated with hydrofluoric acid­HF 40% presented significantly higher contact angle and lowest surface free energy (p < 0.05). The SiO2/Silane presented crystalline SiO2 on the surface. The surface roughness was significantly higher for groups treated with nanofilms (p < 0.05). Shear bond strength was significantly higher for silicatization, HF 40%/silicatization, SiO2/Silane, and SiO2+ZrO2/Silane groups. The proposed treatments with nanofilms had potentially good results without prejudice to the physicochemical characteristics of zirconia. Generally, groups that underwent silica surface deposition and silanization had better bond strength (p < 0.005).

Influence of metal bar lever-arm on screws detorque for dental prosthesis implant supported / Influência do cantilever no destorque de parafusos de barras metálicas utilizadas em próteses do tipo protocolo de Brannemark

Introduction: The cantilever length of implant-supported fixed prosthesis metal structure has been considered an important factor to transfer occlusion forces to the dental implant. Objective: This study evaluated the influence of different extensions of cantilevers of Branemark protocol implant prosthesis when submitted to mechanical thermocycling by screw loosening evaluation. Material and method: The groups G10 (n = 5), G15 (n = 5) and G20 (n = 5) were formed according to the distance in millimeters between the force application site in the cantilever and the center of the last implant. All metal structures (n = 15) were submitted to a 120 N cyclic vertical load in a chewing simulation machine (MSM-Elquip, São Carlos-SP, Brazil) under controlled temperature and moisture conditions. Two hundred and fifty thousand mechanical cycles were performed with a frequency of 2 Hz that simulates a masticatory activity similar to 3 months. To compare the data obtained regarding the loosening of the metal structure screws, implant position and sites of load application, the analysis of variance with two factors and the Tukey test were performed. Result: Statistical analysis showed that the G10 group presented greater torque loss, statistically different from G15 (p = 0.001) and G20 (p = 0.002), and there was no significant difference between groups G15 and G20. Conclusion: It can be concluded from the results that all the screws presented torque loss after simulation of 3 month masticatory activity, suggesting the need for periodical evaluation to prevent failures in the treatment.

Introdução: O comprimento do cantilever da infraestrutura de prótese implanto-suportada tem sido considerado um importante fator de transferência de força de oclusão para o implante dentário. Objetivo: Esse trabalho avaliou a influência das diferentes extensões do cantilever da prótese sobre implantes tipo protocolo de Branemark submetidas à termociclagem mecânica pela avaliação dos afrouxamentos dos parafusos de fixação. Material e método: Os grupos G10 (n=5), G15 (n=5) e G20 (n=5) foram formados de acordo com a distância, em milímetros, entre o local de aplicação de força no cantilever e o centro do último implante. Todas as barras (n=15) foram submetidas a carga vertical cíclica de 120 N em uma máquina de simulação de mastigação (MSM-Elquip, São Carlos/SP, Brasil), em condições de temperatura e umidade controladas. Foram realizados 250 mil ciclos mecânicos com frequência de 2 Hz que simulou uma atividade mastigatória correspondente a 3 meses. Para comparar os dados obtidos quanto à soltura dos parafusos da barra, a posição dos implantes e os locais de aplicação de carga, foi realizada a análise de variância com dois fatores e o teste de Tukey. Resultado: A análise estatística mostrou que o grupo G10 apresentou maior perda de torque, diferente estatisticamente de G15 (p=0,001) e G20 (p=0,002) e que não houve diferença significante entre os grupos G15 e G20. Conclusão: Pode-se concluir que todos os parafusos apresentaram perda de torque após o ensaio simulando uma atividade mastigatória de 3 meses, sugerindo a necessidade de avaliação clínica periódica afim de prevenir fracasso no tratamento.

Bond strength of resin cements to novel materials to intracanal posts applications / Resistência de união de cimentos resinosos a novos materiais para pinos intrarradiculares

Objective: Evaluate the bond strength of resin cements to new materials for application in intraradicular posts. Material and Methods: Five materials were evaluated: fiberglass, PET, polyethylene, polyacetal and PTFE. Two commercial resin cements (Rely X U200 and Rely X Arc) were applied on the test specimens of the materials (9x3mm) and the bonding was evaluated through the shear bond strength test, where the chisel operated with a load of 1kN and a velocity of 0.5mm/min at the cement/material interface. The data were analyzed by the Shapiro-Wilk test, followed by the two-way analysis of variance, performed with the Bonferroni post-test (α=0.05). Results: The glass fiber was statistically different from all evaluated materials (p0.05). Comparing the two cements, a statistical difference was found between Rely X U200 and Arc only for the glass fiber (p=0). Conclusion: PET, polyethylene, polyacetal and PTFE exhibited reduced bond strength compared to the glass fiber (AU)

Objetivo: Avaliar a resistência de união de cimentos resinosos a novos materiais para aplicação em pinos intrarradiculares. Material e método: Foram avaliados cinco materiais: fibra de vidro, PET, polietileno, poliacetal e PTFE. Dois cimentos resinosos comerciais (Rely X U200 e Rely X Arc) foram aplicados sobre os corpos de prova dos materias (9x3mm) e a resistência de união foi avaliada através do teste de cisalhamento, onde o cinzel atuou com carga de 1kN e velocidade de 0,5mm/min na interface cimento/material. Verificada a normalidade dos dados através do teste Shapiro-Wilk, foi realizada a análise de variância de dois fatores com pós-teste de Bonferroni (α=0,05). Resultados: a fibra de vidro foi diferente estatisticamtente de todos os materiais avaliados (p0,05). Comparando-se os dois cimentos, foi encontrada diferença estatística entre o Rely X U200 e Arc apenas para a fibra de vidro (p=0). Conclusão: PET, polietileno, poliacetal e PTFE apresentaram resistência de união reduzida comparando-se à fibra de vidro. (AU)

Tensile Strength of Resin Cements Used with Base Metals in a Simulating Passive Cementation Technique for Implant-Supported Prostheses.

The aim of this study was to analyze the tensile strength of two different resin cements used in passive cementation technique for implant-supported prosthesis. Ninety-six plastic cylinders were waxed in standardized forms, cast in commercially pure titanium, nickel-chromium and nickel-chromium-titanium alloys. Specimens were cemented on titanium cylinders using self-adhesive resin cement or conventional dual-cured resin cement. Specimens were divided in 12 groups (n=8) in accordance to metal, cement and ageing process. Specimens were immersed in distilled water at 37 °C for 24 h and half of them was thermocycled for 5,000 cycles. Specimens were submitted to bond strength test in a universal test machine EMIC-DL2000 at 5 mm/min speed. Statistical analysis evidenced higher tensile strength for self-adhesive resin cement than conventional dual-cured resin cement, whatever the used metal. Self-adhesive resin cement presented higher tensile strength compared to conventional dual-cured resin cement. In conclusion, metal type and ageing process did not influence the tensile strength results.

Tensile Strength of Resin Cements Used with Base Metals in a Simulating Passive Cementation Technique for Implant-Supported Prostheses

Abstract The aim of this study was to analyze the tensile strength of two different resin cements used in passive cementation technique for implant-supported prosthesis. Ninety-six plastic cylinders were waxed in standardized forms, cast in commercially pure titanium, nickel-chromium and nickel-chromium-titanium alloys. Specimens were cemented on titanium cylinders using self-adhesive resin cement or conventional dual-cured resin cement. Specimens were divided in 12 groups (n=8) in accordance to metal, cement and ageing process. Specimens were immersed in distilled water at 37 °C for 24 h and half of them was thermocycled for 5,000 cycles. Specimens were submitted to bond strength test in a universal test machine EMIC-DL2000 at 5 mm/min speed. Statistical analysis evidenced higher tensile strength for self-adhesive resin cement than conventional dual-cured resin cement, whatever the used metal. Self-adhesive resin cement presented higher tensile strength compared to conventional dual-cured resin cement. In conclusion, metal type and ageing process did not influence the tensile strength results.

Resumo O objetivo deste estudo foi analisar a resistência à tração de dois diferentes cimentos resinosos usados na técnica de cimentação passiva de próteses implanto-suportadas. Noventa e seis cilindros plásticos foram encerados em formas padronizadas, fundidos em titânio grau 2 comercialmente puro e ligas de níquel-cromo e níquel-cromo-titânio. Amostras foram cimentadas sobre cilindros de titânio usando um cimento auto-adesivo ou um cimento convencional de dupla polimerização. Os espécimes foram divididos em 12 grupos (n=8) de acordo com o metal, cimento e processo de envelhecimento. Espécimes foram imersos em água destilada a 37 °C por 24 h e metade deles foi termociclado por 5,000 ciclos. Espécimes foram submetidos ao ensaio de tração numa máquina universal de ensaios (velocidade de 5 mm/min). Análise estatística evidenciou maior resistência à tração do cimento auto adesivo do que o cimento convencional de dupla polimerização, independente do metal utilizado. O cimento resinoso auto adesivo apresentou maior resistência à tração do que o cimento convencional de dupla polimerização. O tipo de metal e o processo de envelhecimento não tiveram influência nos resultados.

Localizaçäo da margem cervical de uma restauraçäo: revisäo da literatura / The localization of the gingival margin of the restauration: literature review

Um preparo com finalidade protética deve ser fundamentado em princípios biológicos, mecânicos e estéticos para que possa oferecer um prognóstico favorável. Dentre esses princípios biológicos, um fator muito importante é a localizaçäo da margem cervical, devido à sua intimidade com o tecido periodontal. Essa revisäo da literatura abrange aspectos periodontais relacionados à localizaçäo das margens de restauraçöes protéticas e sua implicaçäo clínica e histológica

Estudo de algumas propriedades físicas de ligas do sistema prata-paládio e prata-cobre. Parte I: elaboração das ligas e análise química por fluorescência de raios x / Study of some physical properties of experimental alloys of silver-palladium and silver-copper systems. Part I: alloy development and chemical analysis by x-ray fluorescence

Com o aumento no preço do ouro, novos sistemas de ligas têm surgido na tentativa de substituí-lo e, muitas vezes, sem estudos aprofundados. Com o objetivo de aprofundar os estudos nessa área de metalurgia, foram desenvolvidas três ligas experimentais, à base de prata, que estão sendo estudadas física e mecanicamente. Este trabalho discorre sobre a análise química qualitativa das ligas através da fluorescência de raios X. Conclui-se que, após as sucessivas fusões, não ocorreram perdas ou contaminações

Estudo de propriedades físicas de ligas experimentais do sistema prata-paládio e prata-cobre. Parte II: análise microestrutural e microdureza Vickers / Study of physical properties of experimental alloys of silver-palladium and silver-copper systems. Part II: microstructural analysis and Vickers microhardness

Num estudo seqüencial sobre aspectos metalúrgicos de ligas à base de prata, foram desenvolvidas três ligas experimentais. Este trabalho tem como objetivo o estudo dessas ligas por difração de raios X para determinar-se a presença de defeitos microestruturais que pudessem afetar as propriedades das mesmas. Foram feitos, também, estudos relacionados à microdureza VICKERS. Concluiu-se que, embora tenham ocorrido alterações microestruturais, estas não comprometeram os valores de microdureza das ligas

Estudo da interface dente-restauração a amálgama por microespectrometria de emissão / Emission microspectrometric study of the amalgam restoration interface

Através de microespectroscopia óptica de emissão as interfaces de restaurações a amálgama foram analisadas em direrentes tempos. Metade dos preparos cavitários receberam tratamento com verniz copal. Em função do tempo houve o aparecimento de produtos de corrosão formados por diversos elementos químicos. O verniz cavitário determinou uma menor presença de mercúrio na interface dente restauração

Ataque eletrolítico de ligas de composições diversas. Parte I: perda de peso dos corpos de prova / Electrolytic etching of different dental alloys. Part I: weight-loss of the samples

Sendo a prótese adesiva uma nova alternativa na área de prótese dental, há necessidade de muitos estudos com o objetivo de alcançar-se aprimoramento técnico. Este trabalho tem o objetivo de estudar o comportamento de uma liga à base de cobre-alumínio e duas à base de níquel-cromo, que foram submetidas a ataque eletrolítico com duas soluções experimentais e uma solução eletrolítica preconizada por Tanaka et alii. Após estudo de perda de peso, pudemos concluir que a composição da liga é um fator fundamental, e que para cada liga, soluções eletrolíticas específicas devem ser desenvolvidas